88%鋁含量鋁礬土熟料 **鋁礬土骨料3-5mm 鋁礬土耐火材料價(jià)格
【鋁礬土產(chǎn)品介紹】：
  
     鋁礬土（aluminous soil；bauxite）又稱(chēng)礬土或鋁土礦，主要成分是氧化鋁，系含有雜質(zhì)的水合氧化鋁，是一種土狀礦物。白色或灰白色，因含鐵而呈褐黃或淺紅色。密度3.9～4g/cm3，硬度1～3，不透明，質(zhì)脆，較難熔化。不溶于水，能溶于硫酸、氫氧化鈉溶液，主要用于煉鋁，制耐火材料。
 
Alumina(aluminous soil; bauxite) also known as alumina and bauxite, main component is aluminum oxide, hydrated alumina system containing impurities, is a kind of clay mineral. White or grey white, due to iron and brownish yellow or light red. Density of 3.9 ~ 4g/cm3, hardness 1 ~ 3, opaque, crisp, very difficult to melt. Insoluble in water, soluble in sulfuric acid, sodium hydroxide solution, mainly used in aluminum smelting, making refractory materials.
 
     耐火材料行業(yè)所稱(chēng)的鋁礬土通常是指煅燒后Al2O3>=48%、而含F(xiàn)e2O3較低的鋁土礦，高鋁礬土熟料是經(jīng)過(guò)煅燒的鋁礬土礦。熟料為灰白淺黃及深灰色，它主要用于高鋁質(zhì)耐火材料，也可用來(lái)制作電熔棕剛玉。
 
Bauxiterefractories industry called usually refers to Al2O3>=48%, and Calcined Bauxite Containing Low Fe2O3, high alumina bauxite is calcined bauxite. Clinker as pale yellow and dark grey, it is mainly used for high aluminum refractory material, also can be used to fabricate fused brown corundum.
 
 
【鋁礬土的分類(lèi)介紹】：
 
熟礬土按煅燒窯爐不同分為:
 
     ①豎爐熟礬土(SHAFT KILN BAUXITE)；
     ②轉(zhuǎn)爐熟礬土(ROTARY KILN BAUXITE)；
     ③倒焰窯礬土(ROUND KILN BAUXITE)。
 
熟礬土按不同用途分為：
 
     ①耐火級(jí)礬土；
     ②研磨級(jí)礬土；
     ③電焊級(jí)礬土。
 
【鋁礬土劃分級(jí)別的標(biāo)準(zhǔn)】：
 
     鋁礬土的種類(lèi)、級(jí)別：
     (1)生礬土，即礬土原礦石(天然沉積巖類(lèi))。
     (2)熟礬土，將生礬土經(jīng)高溫煅燒后(1200～1700℃)稱(chēng)為熟礬土。
     高鋁礬土熟料是按AL2O3含量及Fe2O3、TiO2、Ca O+ Mg O、K2O+Na2O等雜質(zhì)含量和熟料體積密度與吸水等項(xiàng)指標(biāo)來(lái)分級(jí)的。
 
 
【鋁礬土煅燒后，其物化性能變化】：
 
    1、外觀(guān)由原來(lái)的灰、深灰、灰黃、灰白、紅黃等顏色，轉(zhuǎn)變?yōu)榘咨⒚S色、棕紅色、藍(lán)色，而藍(lán)色隨著含鋁量增高而加深。原來(lái)的土狀光澤變?yōu)閯傆窆鉂苫蛴椭鉂桑袝r(shí)表面出現(xiàn)輕微的熔化石或裂縫；
    2、氧化鋁含量增加11～13%,其他雜質(zhì)增加量微；
    3、體積縮小23%左右；
    4、燒失量為14.5%左右；
    5、由一水型鋁石或一水鋁—高嶺石型，轉(zhuǎn)變?yōu)槿嗽靹傆瘛⒛獊?lái)石及少量玻璃相；
    6、硬度由原來(lái)的1～3增加到8以上；
    7、體積密度由原來(lái)的2.5g/cm3左右增加至2.8～3g/cm3以上；
    8、結(jié)晶水、結(jié)構(gòu)水、附著水全部溢出；
    9、結(jié)構(gòu)上由疏、松、軟變?yōu)橹旅軋?jiān)硬；
   10、吸水性降低；抗渣性、抗堿性增強(qiáng)；
   12、強(qiáng)度增加；
   13、滲透性減少；
   14、氣化率減少；
   15、易揮發(fā)成分、易燃燒成分、土氣味*消失；
   16、耐火度達(dá)到1780℃以上。
 
1,from the originalgray, dark gray appearance, gray yellow, gray, red, yellow and other colors, white, beige, into a brown red, blue, and blue as the aluminium content increased and deepened. The original earthy luster to corundum shiny or oily luster, sometimes appear on the surface of mild melt stone or crack;
2, alumina content was increased by 11 ~ 13%, other impurities increase the amount of micro;
3, volume 23%;
4, loss of about 14.5%;
5, by a water-based aluminum stone or a water al kaolinite type, into artificial corundum, mullite and a small amount of glass phase;
6, the hardness from the original 1 to 3 increased to more than 8;
7, the volume density from about 2.5g/cm3 increased to 2.8 ~ 3g/cm3 above;
8, the crystal water, water, water overflow structure attached;
9, the structure by the sparse, loose, soft into dense and hard;
10, water absorption decrease; alkaline slag resistance, resistance to enhance;
12, increase the intensity of;
13, permeability reduction;
14, the gasification rate reduction;
15, volatile component, easy combustion components, rustic flavor completely disappeared;
16, fire resistance up to 1780 ℃.
 
【鋁礬土技術(shù)指標(biāo)】：
 
鋁礬土檢驗(yàn)指標(biāo)：
     (1)高鋁礬土(含Al2O385%以上)要求檢驗(yàn)項(xiàng)目：
         Al2O3  ： 耐火級(jí)85～87%以上，研磨級(jí)86%以上，電焊級(jí)87%以上；
         SiO2    ： 耐火級(jí)6～7%以下，研磨級(jí)5～6%以下；
         Fe2O3  ： 耐火級(jí)1.6～2%以下，**級(jí)2%以下；
         TiO2    :  耐火級(jí)3.5～4%以下，
     電焊級(jí)礬土有的還要求檢驗(yàn)磷、硫、錳等項(xiàng)目；
     B.D.(體積密度)：耐火級(jí)3.10～3.20g/cm3以上，研磨級(jí)、電焊級(jí)不要求檢驗(yàn)該項(xiàng)；
     L.O.I(燒失量)：均為0.3%以下；
 
耐火材料用鋁礬土數(shù)量的技術(shù)條件：  
 
等級(jí) 
化學(xué)成分%
耐火度
體積密度
AL2O3
CaO
Fe2O3
**
>85
<0.6
<2.0
>1790 
>3.0
一級(jí)
>80
<0.6
<3.0 
>1790 
>2.8
二級(jí)甲
70~80
<0.8
<3.0
>1790 
>2.65
二級(jí)乙
60~70
<0.8
<3.0 
>1770
>2.55
三級(jí)
50~60
<0.8
<2.5 
>1770
>2.45

 
粒度：
     按客戶(hù)要求**，一般有自然塊、100mm、50mm、25mm、10mm、5mm、3mm、1mm等。 
 
【包裝運(yùn)輸】：
 
     25kg白色編織袋包裝（也可按客戶(hù)要求包裝）；
     運(yùn)輸儲(chǔ)存期間防止包裝破損，以免漏失或混入雜物；
     運(yùn)輸方式根據(jù)客戶(hù)需求訂貨量安排。
 
【實(shí)圖拍攝】：
 


形狀 : 表面凹凸型 ;
形態(tài) : 層狀 ;
芯材 : MDF ;
撕裂強(qiáng)度 : 5 ;
使用溫度 : 200 ;
拉伸強(qiáng)度 : 16 ;
抗壓強(qiáng)度 : 80 ;
抗彎強(qiáng)度 : 70 ;
斷裂伸長(zhǎng)率 : 6 ;
低溫彎折≤ : 10 ;
等級(jí) : 52 ;
導(dǎo)熱系數(shù)（常溫） : 0.035 ;
材質(zhì) : 鋁 ;
產(chǎn)品類(lèi)別 : 鋁礬土 ;
** : 明悅 ;
產(chǎn)地 : 鞏義 ;
耐火溫度 : 1770～2000℃（℃） ;

鞏義市明悅剛玉制品有限公司 生產(chǎn)耐火材料、棕剛玉、白剛玉、碳化硅、鋁礬土等**消費(fèi)者市場(chǎng)，在消費(fèi)者當(dāng)中享有較高的地位，公司與多家零售商和代理商建立了長(zhǎng)期穩(wěn)定的合作關(guān)系。 鞏義市明悅剛玉制品有限公司實(shí)力雄厚，重信用、守合同、**產(chǎn)品質(zhì)量，品種齊全、價(jià)格合理。以多品種經(jīng)營(yíng)特色和薄利多銷(xiāo)的原則，贏(yíng)得了廣大客戶(hù)的信任。
加工方式 : 來(lái)料加工;OEM加工;手工加工;ODM加工;其他;來(lái)圖加工;來(lái)料代工加工;來(lái)樣加工;
工藝 : 研磨;拋光;干壓成型;其他;
**名稱(chēng) : 明悅
質(zhì)量控制 : 內(nèi)部